Room‐Temperature Freeze Casting for Ceramics with Nonaqueous Sublimable Vehicles in the Naphthalene–Camphor Eutectic System

Freeze casting for Al 2 O 3 was accomplished at room temperature with nonaqueous sublimable vehicles in the naphthalene–camphor eutectic system with a eutectic temperature of 31°C. A fully dense sintered body (>99.5% of theoretical density (T.D.)) was obtained with a eutectic composition vehicle, whereas at most 90% T.D. was obtained with an off‐eutectic (i.e., hypo‐ or hypereutectic) composition vehicle due to formation of large uniquely shaped voids. Microstructural observation suggested that growing pro‐eutectic crystals rejected the suspended Al 2 O 3 particles to form large voids during the solidification process. At the eutectic composition, formation of fine lamellar microstructure in a solidified vehicle is considered to inhibit particle rejection resulting in large voids.