In order to study the degradation of critical temperature T c for a coated conductor using nanorods, the relationship between T c and nanorod shape was investigated by transmission electron microscopy for ErBa 2 Cu 3 O y (Er123) films with BaZrO 3 (BZO) and BaSnO 3 (BSO) nanorods. The dependence of T c on the BZO or BSO content was different, however, the nanorods interface density dependence of T c was the same for both. Thus, the interface density of the nanorods controls T c of the nanorod-added films. The different degradation in T c between the BZO and BSO nanorod-added films originated in differences in the nanorod diameter and density.