Carboxymethyl chitosan (CMCs) is extensively used for wastewater treatment owing to its active functional groups. For improved efficiency, a nanocomposite of two metal oxides, cerium dioxide (CeO 2 ) and iron oxide (Fe 2 O 3 ), was prepared by ball milling. Two loadings (0.15 and 0.3 g) of both metal oxides (CeO 2 and Fe 2 O 3 ) were loaded into CMCs and designated as 0.15CeO 2 /Fe 2 O 3 /CMCs and 0.3CeO 2 /Fe 2 O 3 /CMCs nanocomposites and their photocatalytic activity was evaluated against blank CMCs. CMCs showed flake-like morphology after grinding, which was largely coated by CeO 2 and Fe 2 O 3 . The photocatalytic activity of the nanocomposites was studied under sunlight through the degradation of malachite green (MG) dye under different conditions. The 0.15CeO 2 /Fe 2 O 3 /CMCs nanocomposite was able to degrade the dye completely at 15 mgL -1 after 150 min, while the 0.3CeO 2 /Fe 2 O 3 /CMCs completely degraded in 120 min. The results showed that 400 ppm of the catalyst dose and pH 6 were the optimal conditions for the photocatalytic degradation. For 0.3CeO 2 /Fe 2 O 3 /CMCs, the corresponding constant k values were 0.021, 0.014, and 0.009 min⁻ 1 , respectively. The antibacterial activity was tested against Gram-positive and negative bacteria and the 0.3CeO 2 /Fe 2 O 3 /CMCs showed remarkable antibacterial efficacy. The overall results reveal that the CeO 2 /Fe 2 O 3 /CMCs nanocomposites are efficient photocatalysts for the degradation of MG dyes in wastewater with antibacterial activity and show the potential of alleviating environmental hazards and microbial contamination.
No takes yet. Share an insight, caveat, or question.
Elsherbiny et al. (2026) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: