Research demonstrates improved strength and ductility in titanium alloys with local range order oxygen structure, indicating potential for large-scale applications.
Research on high-performance Ti alloys incorporating oxygen (O) has remained a laboratory procedure and is hindered by the unresolved issue of O segregation-driven failure. Here, we demonstrate that O can tailor a nanoscale local range order O (LRO-O) structure between the oxide and random interstitials in Ti alloy. We introduce 0.36 wt% O into metastable Ti-5Al-5Mo-5V-3Cr alloy using a short-term powder metallurgy approach to produces large-scale materials. The LRO-O structure in designed alloy prevents crack initiation by promoting the active nucleation of <c>-type dislocations and altering the slip modes during tensile and fatigue failure. The alloy has high strength (1.7 GPa), elongation (7.9%), and fatigue strength (1058.3 MPa), which outperforms many high-strength, high-O Ti alloys. Our findings provide a scalable, practical route to superior mechanical properties for Ti alloys without costly alloying elements.
No takes yet. Share an insight, caveat, or question.
Mao et al. (2025) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: