Micro-Tensile Bond Strength of a Mesoporous Bioactive Glass-Containing Universal Adhesive: An In Vitro Study on the Effects of Artificial Aging

Background: We evaluated the immediate and artificially aged micro-tensile bond strengths (μTBS) of Hi-Bond Universal, a universal adhesive containing mesoporous bioactive glass (MBG). Methods: Human dentin specimens were bonded using the following four application modes: Hi-Bond Universal in etch-and-rinse mode, Hi-Bond Universal in self-etch mode, Single Bond 2 in etch-and-rinse mode, and G-ænial Bond in self-etch mode. Specimens were tested either immediately or after artificial aging (thermocycling or water storage). μTBS values were analyzed statistically, and the resin–dentin interfaces were examined using FE-SEM (Field-emission scanning electron microscopy). Results: Results showed that both aging and adhesive mode significantly affected the μTBS (p < 0.0001). Immediately after bonding, etch-and-rinse modes produced significantly higher μTBS than the self-etch modes (p < 0.0001). Artificial aging reduced bond strength by approximately 30–50%; however, the μTBS of Hi-Bond Universal decreased less than that of Single Bond 2 after water storage. FE-SEM analysis also revealed detachment of the hybrid layer in most adhesives following aging; however, Hi-Bond Universal in the etch-and-rinse mode maintained a relatively intact adhesive layer after water storage. Conclusion: Etch-and-rinse application of MBG-containing adhesive may enhance the long-term durability of adhesive restorations.