Fabrication and Characterization of SnSb11Cu6 Babbitt-Infiltrated Open-Cell AlSn6Cu-SiC Matrix Composites

This study investigates the fabrication and performance of a novel composite material by infiltrating SnSb11Cu6 babbitt alloy into an open-cell AlSn6Cu-SiC matrix. The composites, produced via a multi-stage liquid-state processing route, were comprehensively characterized for their microstructural, mechanical, and tribological properties. The inclusion of 5 wt.% silicon carbide reinforcement resulted in a significant improvement in tribological performance under dry-sliding conditions. Specifically, the reinforced composite exhibited a 24.8% reduction in wear and a 10.8% reduction in the coefficient of friction compared to its unreinforced counterpart. Crucially, this enhancement in wear resistance was achieved while the bulk compressive mechanical properties and ductile deformation behavior remained virtually identical to the unreinforced material. Microstructural analysis confirmed that the high-hardness SiC particles act as primary load-bearing agents, shielding the softer metallic matrix from severe wear. These findings demonstrate the successful development of a high-performance composite with enhanced tribological durability without a mechanical trade-off, making it a promising candidate for advanced bearing applications.