Broadband luminescence of Ni²⁺‐doped Zn(GaxAl₁−x)₂O₄‐based glass–ceramics

Ni 2+ ‐doped glass–ceramics containing Zn(Ga x Al x −1 ) 2 O 4 crystals were successfully synthetized using both parent glass crystallization (Technique 1) and a direct doping method also called “frozen sorbet” (Technique 2) to get a ZnGa 2 O 4 crystal/glass composite. The frozen sorbet technique allows the survival of ∼10 nm crystalline particles. Both materials are further crystallized near their respective temperature of crystallization to get glass–ceramics with the stabilization of Zn(Ga x Al x −1 ) 2 O 4 crystals. Although these two materials exhibit the same glass transition temperature, a shift in the crystallization temperature is observed. The glass–ceramics are transparent in the near infrared range, and the Ni 2+ doping provides a broadband emission centered around 1300 nm with a full width at half‐maximum (FWHM) equal to 228 nm. The structure, microstructure, and thermal and optical properties of these materials are discussed in the present study.