Effect of Mg17Al12 Fraction on Mechanical Properties of Mg-9%Al-1%Zn Cast Alloy

In the current study it was observed that the offset yield point of Mg-9%Al-1%Zn alloy was strongly influenced by the connectivity of Mg17Al12. It was suggested that an increase in the fraction of Mg17Al12 from 8% to 11% could lead to the formation of a Mg17Al12 network which resulted in a higher offset yield point. In addition, it was observed that elongation to failure of the Mg-9%Al-1%Zn alloy strongly depended on the fraction of Mg17Al12. Moreover, the apparent toughness showed a strong inverse relation to the secondary dendrite arm spacing. This approach might be extended to forecast the behavior in other magnesium alloys forming a network of the Mg-Al phase.