Si interlayer passivation on germanium MOS capacitors with high-/spl kappa/ dielectric and metal gate

We have demonstrated the advantages of silicon interlayer passivation on germanium MOS devices, with CVD HfO/sub 2/ as the high-/spl kappa/ dielectric and PVD TaN as the gate electrode. A silicon interlayer between a germanium substrate and a high-/spl kappa/ dielectric, deposited using SiH/sub 4/ gas at 580/spl deg/C, significantly improved the electrical characteristics of germanium devices in terms of low D/sub it/ (7/spl times/10/sup 10//cm/sup 2/-eV), less C- V hysteresis and frequency dispersion. Low leakage current density of 5/spl times/10/sup -7/ A/cm/sup 2/ at 1 V bias with EOT of 12.4 /spl Aring/ was achieved. Post-metallization annealing caused continuing V/sub fb/ positive shift and J/sub g/ increase with increased annealing temperature, which was possibly attributed to Ge diffusion into the dielectric during annealing.