Optical Properties of WO₃/Ag/WO₃ Multilayer As Transparent Cathode in Top-Emitting Organic Light Emitting Diodes

We investigated the optical properties of a dielec-tric−metal−dielectric multilayer for the transparent top cathode in top-emitting organic light emitting diodes (TOLEDs). The optical transmittance of the metal layer was enhanced by depositing a dielectric material which had a high refraction index n below and above the metal (Ag) layer. Due to multiple reflections and interferences, the Ag layer sandwiched between dielectric materials with a high value of n can show improved transmittance. Because the WO 3 had a high value of n (>2.0), a thin WO 3 layer could fulfill the optimum zero-reflection condition with an Ag metal layer. Thus, a WO 3 /Ag/WO 3 multilayer should have high transmittance with a low sheet resistance. The optimum thicknesses of both Ag and WO 3 to obtain the best transmittance value were determined by theoretical calculation, and they agreed well with the experimental results. The best results were obtained for the thermally evaporated WO 3 (300 Å)/Ag (120 Å)/WO 3 (300 Å) structure, a high transmittance of ∼93.5% and a low sheet resistance about ∼7.22 ohm/sq were obtained. When the top Al cathode was replaced with the WO 3 /Ag/WO 3 multilayer, the maximum luminance value ( J = 220mA / cm 2 ) increased from 8400 to 11700 cd/m 2, and the power efficiency increased about 26%. To improve the electron injection efficiency at the cathode region, a 20-Å thick Al layer was introduced as an electron injection interlayer between the organic materials and the WO 3 /Ag/WO 3 cathode. Using the Al interlayer decreased the operation voltage at J = 10 mA/cm 2 by 6.9 V. Thus, a WO 3 /Ag/WO 3 with an Al interlayer could promote the transparency of the top cathode and lower the electron injection barrier, enhancing the electroluminescent properties of TOLED.