We carried out tensile impact test and very low speed tensile test on ethylene‐based Ionomers (E/15wt %MAA) to clarify the relation between impact toughness and high‐ordered structure. We also studied the changes in high‐ordered structure under deformation by observing Differential Scanning Calorimetory (DSC) and Small‐Angle X‐ray Scattering (SAXS) of fractured surface. Na Ionomers showed ductile fracture in both high speed tensile impact (3 m/s) and very low speed tensile (2 mm/min). The disappearance of secondary melting point (Ti) in Na Ionomers was due to the destruction of ordered structure surrounding the ionic aggregate. Similar behavior was observed in 60% (or less) neutralized Zn Ionomers. However, 80% neutralized Zn Ionomer showed brittle failure in high‐speed tensile impact, and Ti did not disappear. SAXS studies of Na and Zn Ionomers after fracture, show no change both after molding (no aging) and after aging.
No takes yet. Share an insight, caveat, or question.
Akimoto et al. (2001) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: