Low-Temperature Formation of High-Quality GeO₂ Interlayer for High-κ Gate Dielectrics/Ge by Electron-Cyclotron-Resonance Plasma Techniques

We have fabricated an Al2O3/GeO2gate-dielectric stack on p-type Ge by electron-cyclotron-resonance plasma oxidation and sputtering without external substrate heating. We show that the midgap interface state density at the GeO2/Ge interface is 4.5 × 1010cm-2· eV-1. The hysteresis observed in capacitance-voltage measurements is reduced to 50 mV when the gate bias is swept from accumulation to inversion and back to accumulation or after a single dummy sweep from inversion to accumulation, indicating the possibility that the bulk oxide traps causing the hysteresis are deactivated by the injected holes. The band gap of GeO2was determined by internal photoemission measurements to be 4.7 eV. The conduction- and valence-band offsets at the GeO2/Ge interface are moderately symmetric and large with values of 1.8 and 2.2 eV, respectively. These promising results suggest that low-temperature plasma-grown GeO2is a suitable interlayer between high-dielectric-constant dielectrics and Ge.