Improvement of Interface State and Channel Mobility Using 4H-SiC (0-33-8) Face

In this paper, we characterized MOS devices fabricated on 4H-SiC (0-33-8) face. The interface state density of SiO2/4H-SiC(0-33-8) was significantly low compared to that of SiO2/4H-SiC(0001). The field-effect channel mobility obtained from lateral MOSFET (LMOSFET) was 80 cm2/Vs, in spite of a high p-well concentration of 5x1017 cm-3 (implantation). The double implanted MOSFET (DMOSFET) fabricated on 4H-SiC(0-33-8) showed a specific on-resistance of 4.0 mΩcm2 with a blocking voltage of 890 V.