The Strength of Concentrated Mg-Zn Solid Solutions

Solid solution effects on the hardness and flow stress have been studied for zinc contents between 0.2 and 2.4 at% (0.5 and 6.9 wt%) in Mg. The alloys were grain refined with 0.6 wt% zirconium to ensure a similar grain size at all compositions. The hardness increases with the zinc content as Hv10 (kg mm—2) = 9 Zn (at%) + 33. At low solute concentrations the (0.2%) proof strength does not change significantly with concentration. At concentrations above 0.7 at%, within the supersaturated solid solution region, the rate of solid solution hardening is high, following a c2 rule, where c is the atom fraction of Zn. It is suggested that short-range order may account for most of the observed strengthening in concentrated Mg–Zn alloys.