Highly enhanced thermoelectric and mechanical performance of copper sulfides via natural mineral in-situ phase separation

The precipitates of in-situ phase separation play an important role in enhancing the thermoelectric properties of copper sulfides by suppressing phonon transmission. In this study, Cu1.8S composites were fabricated by melting reaction and spark plasma sintering. The complex structures, micron-PbS, Sb₂S₃, nano-FeS and multiscale pores, originate from the introduction of FePb₄Sb₆S₁₄ into the Cu1.8S matrix. Using effective element (Fe) doping and multiscale precipitates, the Cu1.8S+0.5 wt.% FePb₄Sb₆S₁₄ bulk composite reached a high ZT value of 1.1 at 773 K. Furthermore, the modulus obtained for this sample was approximately about 40.27 Gpa, which was higher than of the pristine sample. This study provides a novel strategy for realizing heterovalent doping while forming various precipitates via in-situ phase separation by the natural minerals, which has been proven to be effective in improving the thermoelectric and mechanical performance of copper sulfides and is worth promoting in other thermoelectric systems.