Analysis of Vertical GaN JBS and p-n Diodes by Mg Ion Implantation and Ultrahigh-Pressure Annealing

We report on vertical GaN junction barrier Schottky (JBS) diodes formed by Mg ion implantation and ultrahigh -pressure annealing (UHPA). The static ON-state characteristics of the diodes show an ideality factor of 1.05, a turn-on voltage of ~0.7 V, a current rectification ratio of~ 10¹¹, and a low differential specific ON-resistance that scales with Schottky stripe width in fair agreement with the analytical model. The reverse leakage dependence on Schottky stripe width also agrees well with the analytical model. Implanted p-n junction diodes fabricated on the same wafer exhibit avalanche breakdown in reverse bias with a positive temperature coefficient, but the forward current is limited by a series barrier. Temperature-dependent current–voltage measurements of th p-n diodes verify the presence of the implanted p-n junction and reveal an additional 0.43-eV barrier, which we hypothesize arises from a p-Schottky contact and forms a second diode back-to-back with the p-n junction. This interpretation is supported by analysis of the capacitance–voltage characteristics of the implanted p-n diodes, epitaxial p-n diodes fabricated with intentional p-Schottky contacts, and comparison to TCAD simulations. Ultimately, the presence of the p-Schottky contact does not hinder JBS diode operation. The use of diffusion-aware designs and/or diffusion reduction represents future directions for Mg implantation technology in GaN power devices.